API 5CT T95 Casing pou sèvis sour se yon gwo -fòs, silfid estrès korozyon krak (SSCC) ki reziste tiyo asye ki fèt espesyalman pou itilize nan gwo-souf (H₂S{-ki gen) lwil oliv ak gaz, apwopriye pou aplikasyon pou pi gwo twou san fon ak ultra-nan kondisyon grav.. Li dwe konfòme yo ak estanda NACE MR0175 / ISO 15156, ki montre ekselan rezistans nan korozyon H₂S, epi li se lajman ki itilize nan pwodiksyon lwil oliv ak gaz nan anviwònman trè asid.
Enkyete sou kowozyon anvlòp pandan min ultra-pi gwo twou san fon? Aman lwil oliv T95, ak yon fòs sede nan 655-758MPa, ofri doub pwoteksyon kont kraze ak sulfid idwojèn.Klike pou w kite enfòmasyon w yo epi resevwa yon twazyèm -rapò tès yo!
API 5CT T95 Espesifikasyon Tubing Aman
| Atik | Paramèt |
|---|---|
| Estanda | API 5CT, ISO 11960 |
| Klas | T95 |
| Sede fòs | 655–758 MPa (95–110 ksi) |
| Fòs rupture | Pi gran pase oswa egal a 758 MPa |
| Tretman Chalè | Trempe ak tanperaman (Q&T) |
| Aplikasyon Sèvis | Sour Service (anviwònman H₂S) |
| Egzijans dite | Mwens pase oswa egal a 25 HRC oswa Mwens pase oswa egal a 255 HBW |
| Sètifikasyon | NACE MR0175/ISO 15156, te pase tès SSCC |
Tablo Dimansyon Tubing Aman T95
| OD (nan) | OD (mm) | Epesè mi komen (mm) | Apwopriye byen pwofondè |
|---|---|---|---|
| 4.5 | 114.3 | 8.56, 9.17, 10.92 | Mwayen-pi gwo twou san fon |
| 5.5 | 139.7 | 9.17, 11.05, 13.72 | Pwi fon |
| 7 | 177.8 | 10.36, 12.65, 15.88 | Pwi fon |
| 9 5/8 | 244.5 | 11.05, 13.84, 15.11 | Pwi ultra-fon |
| 13 3/8 | 339.7 | 12.70, 15.88, 19.05 | Pwi ultra-fon |
API 5CT Klas T95 Aman Tubing Steel Kòd Koulè
| Klas | Mak koulè (pentire sou tou de bout) |
|---|---|
| T95 | Wouj ak Blan Band |
API 5CT Gr. T95 Tib Chimik Konpozisyon Tablo
| Eleman | Kontni (%) | Nòt |
|---|---|---|
| C | Mwens pase oswa egal a 0.35 | Amelyore fòs, kontwole hardenability |
| Mn | 0.25–1.20 | Amelyore severite ak travayabilite |
| Kr | 0.40–1.50 | Ogmante rezistans korozyon ak hardenability |
| Mo | 0.15–0.85 | Amelyore estabilite tanperaman ak rezistans SSCC |
| Ni | Mwens pase oswa egal a 0.99 | Amelyore solidite tanperati ki ba- |
| Cu | Mwens pase oswa egal a 0.30 | Anpeche korozyon atmosferik |
| P | Mwens pase oswa egal a 0.015 | Eleman danjere, entèdi kontwole |
| S | Mwens pase oswa egal a 0.010 | Kòz frajil cho, kenbe ba |
| V, Ti, Al | Tras | Rafineman grenn jaden, amelyorasyon pèfòmans |
API 5CT T95 Pwopriyete mekanik tib
| Pwopriyete | Egzijans |
|---|---|
| Fòs Sede (YS) | 655-758 MPa |
| Fòs rupture (TS) | Pi gran pase oswa egal a 758 MPa |
| Elongasyon (50mm kalib) | Pi gran pase oswa egal a 10% |
| Dite | Mwens pase oswa egal a 25 HRC / Mwens pase oswa egal a 255 HBW |
| Enèji enpak (-10 degre) | Pi gran pase oswa egal a 27 J mwayèn, yon sèl valè Pi gran pase oswa egal a 20 J (si sa nesesè) |
| Rezistans SSCC | Pase NACE TM0177 Metòd A |
API 5CT T95 Gwosè Tiyo Aman nan MM Tablo
| Gwosè (pous) | OD (mm) | Ranje pwa (kg/m) | WT komen (mm) |
|---|---|---|---|
| 2 3/8 | 60.3 | 4.85–6.45 | 5.54, 6.91 |
| 2 7/8 | 73.0 | 6.40–8.65 | 6.91, 8.94 |
| 3 1/2 | 88.9 | 7.90–11.50 | 7.62, 9.52 |
| 4 1/2 | 114.3 | 10.20–16.13 | 8.56, 10.92 |
| 5 1/2 | 139.7 | 13.60–20.78 | 11.05, 13.72 |
| 7 | 177.8 | 18.00–28.10 | 12.65, 15.88 |
| 9 5/8 | 244.5 | 24.50–40.00 | 13.84, 15.11 |
| 13 3/8 | 339.7 | 48.00–72.00 | 15.88, 19.05 |
API 5CT T95 OCTG Tolerans
| Atik | Tolerans admisib |
|---|---|
| Dyamèt Eksteryè (OD) | ±0.79 mm (mwens pase oswa egal a 101.6 mm); +1.0% / -0.5% (Pwose oswa egal a 114.3 mm) |
| Epesè miray (WT) | -12.5% |
| Longè (R1) | 4.88–7.62 m |
| Longè (R2) | 7.62–10.36 m |
| Longè (R3) | 10.36–14.63 m |
| Pwa (pa moso) | +6.5% / -3.5% |
| Dwat | Mwens pase oswa egal a 0.2% nan longè |
| Thread Taper | 1:16 ± 0.002 pous/pous |
API 5CT T95 Aman Tubing Metòd enspeksyon
Analiz konpozisyon chimik: Analiz espektak pou chak chalè asire eleman kle tankou C, Cr, ak Mo satisfè espesifikasyon yo.
Tès mekanik:
Tès Tensile
Tès dite (Rockwell C, HBW)
Tès rezistans enpak (Charpy V-dan, si sa nesesè)
Tès Sulfide Estrès Kowozyon Cracking (SSCC).: Fè selon NACE TM0177 Metòd A, ki dire plis pase 720 èdtan nan solisyon H₂S-.
Tès ki pa-destriktif (NDT):
Tès à (UT): Longitudinal ak transverse defo deteksyon
Eddy Current Testing (ET): Pou tib
Tès patikil mayetik (MT): Sifas enspeksyon krak sou zòn Threaded
Enspeksyon dimansyon ak pwofil: OD, epesè miray, dwat, presizyon fil
Tès idrostatik: Fè sou chak tiyo sèl, presyon pa mwens pase 80% nan espesifye minimòm rezistans presyon entèn
GNEE API 5CT OCTG faktori
FAQ
Ki sa ki tolerans OD a?API 5CT?
Nan estanda API 5CT, tolerans dyamèt ekstèn tiyo asye divize an de kalite selon gwosè diferan: pou tiyo asye ak yon dyamèt ekstèn mwens pase oswa egal a 114.3 mm (4 1/2 pous), tolerans dyamèt ekstèn lan se ± 0.79 mm; pou tiyo asye ak yon dyamèt ekstèn ki pi gran pase oswa egal a 114.3 mm, tolerans la se +1.0% / -0.5%.
Ki sa ki API 5CT vle di?
API 5CT se yon abrevyasyon pou Spesifikasyon American Petroleum Institute 5CT, ki vle di Spesifikasyon pou bwat ak tib. Li devlope pa Enstiti Ameriken Petwòl (API) e li se yon estanda teknik entènasyonalman rekonèt ki itilize nan endistri lwil oliv ak gaz pou kontwole aman ak tib yo itilize nan pwi lwil oliv.
Baj popilè: api 5ct t95 aman pou sèvis tounen, Lachin api 5ct t95 aman pou manifaktirè sèvis tounen, Swèd, faktori