L80-13Crtotalman depaseL80-9Cran tèm de rezistans korozyon, kontni alyaj, ak kondisyon opere aplikab. Malgre ke tou de fè pati nan klas asye L80, L80-13Cr{-gras a pi wo kontni li yo Kwòm, molybdène, ak nikèl-se espesyalman enjenyè pou anviwònman ki pi grav korozivite.
Evite Reta Pwojè: Stock Pare nan API 5CT L80-9Cr & 13Cr Disponib.
API 5CT L80-9Cr & 13Cr boîtierKonparezon Chimik Konpozisyon
| Eleman (poids%) | L80-9Cr | L80-13Cr |
| Kabòn (C) | Mwens pase oswa egal a 0.15 | 0.15 ~ 0.22 |
| Kwòm (Cr) | 8.00 ~ 10.00 | 12.00 ~ 14.00 |
| Molybdène (Mo) | 0.90 ~ 1.10 | Pa Espesifye (Tipik <0.05) |
| Manganèz (Mn) | 0.30 ~ 0.60 | 0.25 ~ 1.00 |
| Silisyòm (Si) | Mwens pase oswa egal a 1.00 | Mwens pase oswa egal a 1.00 |
| Nikèl (Ni) | Mwens pase oswa egal a 0.50 | Mwens pase oswa egal a 0.50 |
| Fosfò (P) | Mwens pase oswa egal a 0.020 | Mwens pase oswa egal a 0.020 |
| Souf (S) | Mwens pase oswa egal a 0.010 | Mwens pase oswa egal a 0.010 |
| Kwiv (Cu) | Mwens pase oswa egal a 0.25 | Mwens pase oswa egal a 0.25 |
API 5CT L80-9Cr & 13Cr OCTGKonparezon pwopriyete mekanik
| Atik Pwopriyete | L80-9Cr | L80-13Cr |
| Fòs Sede (Rt0.5) | 552 ~ 655 MPa (80 ~ 95 ksi) | 552 ~ 655 MPa (80 ~ 95 ksi) |
| Fòs rupture (Rm) | Pi gran pase oswa egal a 655 MPa (95 ksi) | Pi gran pase oswa egal a 655 MPa (95 ksi) |
| elongasyon (A) | Pou chak fòmil API 5CT | Pou chak fòmil API 5CT |
| Max dite | Mwens pase oswa egal a 23 HRC | Mwens pase oswa egal a 23 HRC |
| Varyasyon dite | Mwens pase oswa egal a 6.0 HRC (-Koup transvèsal) | Mwens pase oswa egal a 6.0 HRC (-Koup transvèsal) |
| Mikwostrikti | Tanpered Martensite | Tanpered Martensite |
API 5CT L80-9Cr & 13Cr san pwoblèm lwil oliv bwat tiyoPèfòmans Kowozyon ak Limit Sèvis
| L80-9Cr | L80-13Cr | |
| Rezistans prensipal |
CO2CO2 Kowozyon |
CO2CO2 Kowozyon |
|
CO2CO2 Presyon pasyèl (PCO2PCO2 ) |
Modere (sijere < 2 psi) | Segondè (kapab depase 30 psi) |
|
H2SH2S Presyon pasyèl (PH2SPH2S ) |
tras (< 0.01 psi) | Trè ba (< 0.05 psi); prone to SSC |
| klori (
Cl−Cl− ) Konk. |
Sansib (risk pou pitting) | Sansib (Fim kraze nan gwo konsantrasyon) |
| Tanperati sèvis maksimòm. | ~ 120 degre - 150 degre | ~ 150 degre - 180 degre |
| pH Anviwònman | > 4.5 | > 3.5 |
| Estabilite fim pasif | modere; Nivo Cr pi ba pase "pur" papòt | High; Cr >12% fòme stab Cr2O3Cr2O3 |
| Molybdène (Mo) Wòl | Amelyore rezistans pitting | Konte sou Cr (sòf si Super 13Cr) |
API 5CT L80-9Cr & 13Cr lwil oliv byen amanKarakteristik fizik ak fabrikasyon
| Atik | L80-9Cr | L80-13Cr |
| Tretman Chalè | Aparèy + Tanperaman (Q+T) | Aparèy + Tanperaman (Q+T) |
| Dansite (
ρρ ) |
~ 7.75 g/cm3g/cm3 |
~ 7.70 g/cm3g/cm3 |
| Modil elastik (E) | ~ 210 GPa | ~ 200 GPa |
| Ekspansyon tèmik | Yon ti kras pi wo pase asye kabòn | Siyifikativman pi ba pase asye kabòn |
| Kondisyon NDT | Tout longè EMI / UT | Tout longè EMI / UT |
| Koneksyon fil | Anjeneral Koneksyon Premium | Anjeneral Koneksyon Premium |
| Galling Rezistans | Modere | Pòv(Segondè Cr gen tandans fè grip) |
| Pri relatif | Pi ba (Altènatif ekonomik) | Pi wo (Solisyon estanda) |
GNEE API 5CT aman ak tib nan stock
GNEE liy pwosesis tiyo
GNEE Pipe tès ak ekipman enspeksyon
Zewo -Angajman Defo: 100% konplè-Kò UT & EMI teste.
FAQ
Ki sa ki asye L80?
Low Alloy Steel
L80 seyon fe alyaj ba-ki itilize prensipalman nan aplikasyon pou lwil oliv ak gaz, patikilyèman pou anvlòp ak tib.
Ki sa ki ekivalan L80 a?
L80 se anjeneral yo itilize nan pwi ak anviwònman tounen (sulfid idwojèn), aman, tib pwodiksyon, stock kouple, jwenti pup, ak divès kalite Pwodwi pou Telefòn downhole. L80 (API 5CT) se yon asye kabòn mwayen epi li ekivalan aSAE 4140.
Ki sa ki L80 vle di?
L80 : Sa vle diyo pral kenbe yon minimòm de 80% nan flux lumineux pou yon peryòd defini bay maksimòm tanperati anbyen an.