A53 Klas B Konpozisyon chimik (%)
| konpozisyon | C | Mn | P | S | Kr | Ni | Taks | Mouvman | V | Plis | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| Kalite S | Min | - | - | - | - | - | - | - | - | - | Cr+Ni+Cu+V Mwens oswa egal a 1 |
| Maks | 0.3 | 1.2 | 0.05 | 0.045 | 0.4 | 0.4 | 0.4 | 0.15 | 0.08 |
| konpozisyon | C | Mn | P | S | Kr | Ni | Taks | Mouvman | V | Plis | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| Kalite E | Min | - | - | - | - | - | - | - | - | - | Cr+Ni+Cu+V Mwens oswa egal a 1 |
| Maks | 0.3 | 1.2 | 0.05 | 0.045 | 0.4 | 0.4 | 0.4 | 0.15 | 0.08 |
A500 konpozisyon chimik (%)
| konpozisyon | C | sizo | Mn | P | S | Taks | Mouvman | Kòm | N | Tibèkil | V | Nòb | Al | Plis |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Min | - | - | - | - | - | - | - | - | - | - | - | - | - | Nb+Ti+V Mwens pase oswa egal a 0.15 |
| Maks | 0.22 | 0.9 | 1.6 | 0.05 | 0.05 | 0.35 | 0.1 | 0.08 | 0.012 | 0.025 | 0.1 | 0.1 | 0.025 |
Pwopriyete mekanik A53 Klas B
|
Fòs rupture |
Pwen sede σs Mpa |
Elongasyon nan kraze oswa elongasyon δ % |
|---|---|---|
| Pi gran pase oswa egal a 415 | Pi gran pase oswa egal a 240 | ① |
① Lè longè kalib L0=2pous (50mm), fòmil kalkil elongasyon minimòm δ la se jan sa a:
δ=625000[1940]A0.2/U0.9
Ki kote:
Zòn yon mwens pase 0.75 pous2[500mm]2] ak zòn transvèsal echantiyon an, kalkile lè l sèvi avèk dyamèt ekstèn tiyo espesifye oswa lajè nominal echantiyon an ak epesè miray tiyo espesifye a, valè kalkile a awondi a 0.01in.2[1mm]2];
U-minimòm fòs rupture, psi [MPa]
Remak: 1940 yo itilize pou metrik
Pwopriyete mekanik nan A500
| Fòs rupture σb Mpa |
Pwen sede σs Mpa |
Elongasyon nan kraze oswa elongasyon δ % |
|---|---|---|
| Pi gran pase oswa egal a 600 | Pi gran pase oswa egal a 500 | Pi gran pase oswa egal a 14 |
GNEE ASTM A53 GRB Tiyo pou vann